RTV60 001-Kit (1.0LBS-0.454KG)

RTV60 001-Kit (1.0LBS-0.454KG)

Availability: In stock



Manufacturer: Momentive
Part #: RTV 60, LB KIT
SKU: MOMRTV 60, LB KIT
Selling Unit: EA

This product is considered hazardous.
A $25 packaging fee will be added by VMS Aircraft Company
A $25 shipping/handling fee will be added by FedEx



Price: $72.39

Details

High Temperature Two-Part Silicone Elastomer
RTV31, RTV60 and RTV88 silicone rubber compounds are high temperature two-part silicone elastomers. They are supplied ready-to-use with a base compound and DBT (dibutyl tin dilaurate) as the standard curing agent. DBT is suitable for most applications, however other catalysts are available to facilitate deep section cure, faster cure and automated mixing. RTV31, RTV60 and RTV88 silicone rubber compounds differ primarily in viscosity in the uncured state.

Vms Part NumberVMS-0984-00162
NumberRTV 60
Other Product Identifier9464
Short DescriptionHigh Temperature Two-Part Silicone Elastomer
Part NumberRTV 60, LB KIT
AppearanceFlowable
Coefficient Of Expansion20 x 10^-5 cm/cm, ° C (11 x 10^-5 in/in, °F) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
ColorRed
ConsistencyPourable
Cure ChemistryAlkoxy
Cure SpeedSlow Cure
Cure SpeedSlow Cure
Unit of MeasureEA
Cure Time24 @ 25C (77F), hrs (UNCURED PROPERTIES OF RTV BASE WITH 0.5% DBT CURING AGENT ADDED)
ManufacturerMomentive
Cure Type2 Part Condensation
Dielectric Constant4 @ 1000 Hz (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Dielectric Strength17.7 kV/mm (450 Volts/mil) (1.9 mm thick) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Dissipation Factor0.02 @ 1000 Hz (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Durometer Hardness57 Shore A (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Elongation120% (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Mixed ColorRed
Per Package12
Per Case12
RegionGlobal
Shrinkage0.6% (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Specific Gravity1.48
Specific Heat0.35 cal/gm, ° C (-0.35 BTU/lb, °F) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Tear Strength7 kg/cm (40 lb/in) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Tensile Strength70 kg/cm^2 (990 psi) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Thermal Conductivity0.00074 gm-cal/sec, cm^2, ° C/cm (0.18 Btu/hr/ft^2, °F/ft) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Useful Temperature Range-54 to 26 ° C (-65 to 500 ° F) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Viscosity47,000 cps
Volume Resistivity4.4 x 10^14 ohm-cm (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Work Time2 at 25C (77F), Hours (UNCURED PROPERTIES OF RTV BASE WITH 0.5% DBT CURING AGENT ADDED)