High Temperature Two-Part Silicone Elastomer
RTV31, RTV60 and RTV88 silicone rubber compounds are high temperature two-part silicone elastomers. They are supplied ready-to-use with a base compound and DBT (dibutyl tin dilaurate) as the standard curing agent. DBT is suitable for most applications, however other catalysts are available to facilitate deep section cure, faster cure and automated mixing. RTV31, RTV60 and RTV88 silicone rubber compounds differ primarily in viscosity in the uncured state.

Vms Part NumberVMS-0984-00215
NumberRTV 88
Other Product Identifier9531
Short DescriptionHigh Temperature Two-Part Silicone Elastomer
Part NumberRTV 88, LB KIT
AppearancePaste
Coefficient Of Expansion20 x 10^-5 cm/cm, ° C (11 x 10^-5 in/in, °F)(0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
ColorRed
ConsistencySpreadable Paste
Cure ChemistryAlkoxy
Cure SpeedSlow Cure
Cure SpeedSlow Cure
Unit of MeasureEA
Cure Time24 hrs at 25C (77F) (UNCURED PROPERTIES OF RTV BASE WITH 0.5% DBT CURING AGENT ADDED)
ManufacturerMomentive
Cure Type2 Part
Dielectric Constant4.3 @ 1000 Hz (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Dielectric Strength17.4 kV/mm (440 Volts/mil) (1.9 mm thick) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Dissipation Factor0.03 @ 1000 Hz (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Durometer Hardness58 Shore A (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Elongation120% (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Mixed ColorRed
Per Package12
Per Case12
RegionGlobal
Shrinkage0.6% (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Specific Gravity1.47
Specific Heat0.35 cal/gm, °C (0.35 BTU/lb, °F) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Tear Strength8 kg/cm (42 lb/in) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Tensile Strength59 kg/cm^2 (830 psi) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Thermal Conductivity0.00074 gm-cal/sec, cm^2, °C/cm (0.18 Btu/hr/ft2, °F/ft) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Useful Temperature Range-54 to 260 ° C (-65 to 500 ° F) (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Viscosity880,000 cps
Volume Resistivity2.8 x 10^14 ohm-cm (0.5 wt. % DBT Curing Agent added, cured 7 days at 25C (77F) and 50% R.H.)
Work Time0.75 Hours at 25C (77F) (UNCURED PROPERTIES OF RTV BASE WITH 0.5% DBT CURING AGENT ADDED)
Quantity In Stock5 Weeks